• Polyurethane Odourless Waterproofing Coating
enquire
Polyurethane Odorless Liquid is a high solids, cold-liquid waterproofing solution

Polyurethane Odourless Waterproofing Coating is a high solids, cold-liquid waterproofing solution

Polyurethane Odorless Liquid waterproofing membrane coating

This waterproofing membrane coating is quickly resistant to rainfall and cures in just 24 hours

Polyurethane Odorless Liquid waterproofing for car parks, metal cladding and roofs

It's an ideal waterproofing solution for metal cladding, car parking and solves the problems associated with the long-term waterproofing of flat, pitched and domed roofs

Polyurethane Odorless liquid forms a completely seamless membrance and incorporates details with ease

This technology forms a completely seamless membrane and incorporates upstands and detailing work with ease

This Waterproofing Coating emits no solvent odour during application

It's compatible with most existing roof membranes – even on weathered and damaged substrates

Polyurethane Odorless Liquid is highly resistant to ponded water and provides the perfect shield against future leaks

This protective coating is highly resistant to ponded water, providing the perfect shield against future leaks

Polyurethane Odorless Liquid is a high solids, cold-liquid waterproofing solution
Polyurethane Odorless Liquid waterproofing membrane coating
Polyurethane Odorless Liquid waterproofing for car parks, metal cladding and roofs
Polyurethane Odorless liquid forms a completely seamless membrance and incorporates details with ease
Polyurethane Odorless Liquid is highly resistant to ponded water and provides the perfect shield against future leaks

Polyurethane Odourless Waterproofing Coating is a cold applied, odour free waterproofing solution for refurbishment and new build structures.

This Waterproofing Coating has all the benefits of a polyurethane liquid applied roof system but emits no solvent odour during application. This makes it especially useful for buildings where solvent odours are prohibitive. It’s a high solids, cold-liquid waterproofing solution that creates a seamless finish which is impermeable soon after application. This protective coating is highly resistant to ponded water, providing the perfect shield against future leaks. It solves the problems associated with the long-term waterproofing of flat, pitched and domed roofs and is compatible with most existing roof membranes – even on weathered and damaged substrates.

This waterproofing membrane coating is an ideal long-term solution. Unlike conventional roofing systems, it forms a completely seamless membrane on the roof and incorporates details with ease and cures in just 24 hours. The Fibretex liquid applied component provides waterproofing for upstands and detailing work.

Polyurethane Odourless Waterproofing Coating key benefits:

  • Zero solvent odour during installation
  • Quickly resistant to rainfall and cures in just 24 hours
  • Excellent resistance to ponded water
  • Seamless – no joints or seams
  • Encapsulates an entire roof seamlessly –  including any plant and protrusions – forming a breathable, waterproof barrier
  • Easily maintained
  • Can be applied over most existing roof surfaces and is suitable for  many types of traditional roofing materials including felt, asphalt, bitumen, asbestos cement sheet, fibre cement sheet, concrete, single ply membranes and profiled metal sheets.

Polyurethane Odourless Waterproofing Coating application areas include:

  • Flat and pitched roofing areas
  • Metal Cladding
  • Car Parking
  • Gutters
  • Vents and pipes
  • Rainwater outlets
  • Parapet walls
  • Rooflights
  • HVAC and ducting
  • Many existing substrates

For all your Polyurethane Odourless Waterproofing Coating needs, get in touch with Cactus Industrial today.

enquire

Polyurethane Odourless Waterproofing Coating system uses Multi Substrate Primer, a high performance universal primer that provides excellent binding and adhesion to most substrates including plastics, wood, mineral substrates, ceramic tile, copper, zinc, brass, steel, galvanised steel, aluminium etc. Winter painting operations are possible due to tolerance of low temperature/high humidity conditions.

Typical Thickness 100 microns dft from 145 microns wet
Theoretical Coverage 7 square metres per litre
Practical Coverage Reduce above by up to 20%
Mix Ratio
(by volume)
2.75 : 1.25
Base : Activator
Method of Application Brushing or spraying for structural steel work. Airless spray preferred for large areas such as storage tanks.
Drying Time 8 – 16 hours (Touch Dry)
24 hours (Hard Dry)
Pack Size 4 litre unit

 

 

Polyurethane Odourless Waterproofing Coating Binder Sealer & Primer is an all-aliphatic stabilising sealer and primer for use on a wide range of substrates such as concrete, asphalt, bitumen, felt, asbestos, plaster, render, etc.

Intended Uses For use on a wide range of substrates such as concrete, asphalt, bitumen, felt, asbestos, plaster, render etc.
Theoretical Coverage Up to 12 square metres/litre/coat. (low porosity substrates)
Practical Coverage Typically 10 square metres/litre on porous and/or rough surfaces.
Varies according to porosity, surface profile, etc
Mix Ratio
(by weight/volume)
10 : 1
Base : Activator
Method of Application Brush, roller.
Two coats may be necessary on highly porous substrates.
Drying Time
(at 20°C substrate temperature)
2 hours (Touch Dry)

3 hours (Hard Dry)

Pack Size 5 litres

Polyurethane Odourless Waterproofing Coating Embedment Coat is for application in conjunction with Elastamat glass fibre reinforcement as the basecoat in this Waterproof Roofing system.

Typical Thickness 0.9 – 1.1mm dft including reinforcement
Theoretical Coverage 0.8 – 1.0 square metres per litre
Practical Coverage Dependent on surface profile
Method of Application Brush or roller
Drying Time 8 hours (Touch Dry)

24 hours (Hard Dry)

Pack Size 12.5 litres

Polyurethane Odourless Waterproofing Coating Top Coat is a cold applied single pack, ultra high solids moisture activated elastomeric urethane coating. 

Typical Thickness 0.45 – 0.9mm dft per coat
(depending on the system)
Theoretical Coverage 1 – 2 square metres per litre coat
Practical Coverage Dependent on surface profile, reinforcement where applicable etc.
Method of Application Brush or roller. May be used as the carrier for Elastamat glass fibre reinforcement matting on localised repairs.
Do not apply is rain is imminent
Drying Time 8 hours (Touch Dry)

24 hours (Hard Dry)

Pack Size 12.5 litres

Polyurethane Odourless Waterproofing Coating  Fibretex is a high build, heavy duty, fibre loaded stripe coating, to be used prior to over-coating.

Typical Thickness 0.9mm dft per coat
(depending on system)
Theoretical Coverage 1 square metre per litre per coat
Practical Coverage Dependent on surface profile, reinforcement where applicable etc.
Method of Application Brush or roller. May be used as the carrier for Elastamat glass fibre reinforcement matting on localised repairs.
Drying Time
(at 20°C and 1.0mm wet film)
8 hours (Touch Dry)

24 hours (Hard Dry)

Overcoating interval (24 hours minimum; 7 days maximum)

Pack Size 5 litres

12.5 litres

ARC 858 high strength bonding polymer seals, shims and bonds new plates to a prepared surface on an offshore platform

Plate Bonding – Cactus ARC 858

Live Leak Sealing A Drains Line

Bristle Blaster, Power Plant

View Similar Products...

PMMA Glow In The Dark application shown in daylight and darkness

PMMA Glow In The Dark

PMMA Glow In The Dark technology absorbs UV radiation, daylight or artificial light to provide a light source in the dark. Th

Self-Levelling Mortar Rapid Curing PMMA Technology is ideal solution for offshore deck, laydown and walkway areas

Epoxy High Strength Resin Screed

Epoxy High Strength Resin Screed is an epoxy levelling mortar and mortar screed that resurfaces and protects large areas from

flange face corrosion repair kit featured image

Flange Face Forming Kit 234

One convenient kit for complete in-situ flange face forming repair. It packs all the equipment you'll need for rapid, effectiv

Need more info on our coatings & composites?

contact us