• ARC HT-T High Temperature Resistant Trowel Grade Coating
enquire
ARC HT-T High Temperature Resistant Trowel Grade Coating is applied to the nozzle of a first stage separator

The nozzle of a first stage separator is coated with High Temperature Erosion Control Coating

ARC HT-T high temperature resistant coating is applied to protect this metal equipment from erosion

The high temperature resistant coating is easily applied by trowel and is effective in immersed aqueous solution conditions up to 110°C (230°F)

ARC HT-T High Temperature Resistant Trowel Grade Coating is applied to the nozzle of a first stage separator
ARC HT-T high temperature resistant coating is applied to protect this metal equipment from erosion

ARC HT-T High Temperature Resistant Coating is an advanced ceramic Trowel Grade Coating.

This High Temperature Resistant Coating is formulated to protect equipment from corrosion and erosion in elevated temperature water solution immersion. It’s easily applied by trowel or plastic applicator tool to rebuild and protect new and old equipment.

ARC HT-T is a 100% solids, VOC free , spark testable (per NACE SP0188) coating application. This ceramic reinforced abrasion resistant epoxy is strong, tough and durable. It resists cold wall delamination. The cured product also provides outstanding blister resistance with a high gloss finish.

This High Temperature Resistant, high viscosity technology ensures high adhesive strength and exceptional corrosion and erosion protection to high temperature equipment handling water solutions.

ARC HT-T is a Trowel Grade Coating while ARC HT-S is a Spray Coating. Both get to work in elevated temperatures.

ARC HT-T High Temperature Resistant Coating is designed to:

  • Rebuild and protect new and old metal equipment
  • Perform in immersed aqueous solution conditions up to 110°C (230°F)
  • Safely and easily apply by trowel

ARC HT-T High Temperature Resistant Coating application areas include:

  • Oil/water separators
  • Pressure vessels
  • Pumps
  • Oil/gas separators
  • Tanks and vessels
  • Valves
  • Heat exchangers
  • Desalting vessels
  • Crystalizers
enquire
Mix Ratio A:B By Weight 14.0 : 1

By Volume 5.7 : 1

Working Time 5 litres is 60 mins at 16°C (60°F)

5 litres is 45 mins at 25°C (77°F)

Curing Schedule Tack Free at 16°C (60°F) is 8 hours

Light Load at 16°C (60°F) is 18 hours

Overcoat Begin at 16°C (60°F) is 8 hours

Overcoat End at 16°C (60°F) is 72 hours

Cure For Service at 16°C (60°F) is 84 hours

Pull Off Adhesion (ASTM D 4541)

316.9 kg/cm² (31.1 MPa)

4510 psi

Vertical Sag Resistance

at 21°C (70°F) and 1.25mm (50 mil)

No Sag
Maximum Temperature

(Dependent on service)

Wet Service is 110°C (230°F)

Dry Service is 150°C (302°F)

Cured Density 2.22 gm/cc

137.32 lb/ cu.ft.

Packaging and Coverage
Nominal, based on a 750 µm (30 mil) DFT
5 litre kit covers 6.67 m² (71.76 ft²)
ARC 858 high strength bonding polymer seals, shims and bonds new plates to a prepared surface on an offshore platform

Plate Bonding – Cactus ARC 858

Live Leak Sealing A Drains Line

The Bristle Blaster surface preparation tool is used in pipeline maintenance and repair

Bristle Blaster, Steel Construction

View Similar Products...

Glow In The Dark Luminescent Coating PMMA Technology Application shown in daylight and darkness

Glow In The Dark Luminescent Coating PMMA Technology

Glow In The Dark Luminescent Coating PMMA Technology absorbs UV radiation, daylight or artificial light to provide a light sou

ARC S2 Ceramic Reinforced Coating is applied to transport screw trough of a wastewater plant

ARC S2 Ceramic Reinforced Coating

ARC S2 Ceramic Reinforced Coating is a thin film industrial coating. It's designed to protect structures and equipment agains

ARC 10 Metal Repair Compound is used as an effect flange face forming and flange repair technology

ARC 10 Metal Compound

ARC 10 Metal Compound is a machinable polymer alloy blend. This metal repair and rebuilding compound is used to resurface sc